9000 - 100 Percent Solids Epoxy Mastic

100% Solids Epoxy Mastic - 

100% solids two part epoxy system for bonding and filling concrete and other substrate. Rhino 9000 offers long work life, quick cure, good chemical resistance and low odor during application. Rhino 9000 is a syntactic, light weight mastic with excellent thixotropy, it trowels easily on vertical and overhead surfaces. Easy to use 2:1 volume mixing and color coding ensure a proper mix every time. DOT and IATA non-corrosive for ease of transportation.

_images/medium/01040907379000 380x308 template.jpg

Suggested Uses

Rhino 9000 is intended primarily as an adhesive for bonding similar and dissimilar substrates. Due to its moisture tolerance and chemical resistance, this system finds wide application in concrete repair. When used in conjunction with Rhino 1501 primer, the material tolerates hydrostatic pressure(s) typically found in concrete sewer and wastewater applications.

Benefits & Features

• Easy to use 2:1 maix ratio
• 40-70 minutes of working life (time varies according to temperature and batch size)
• Use at temperatures above 45°F (7°C) and lass than 100°F (38°C)
• Typically cures in 6-8 hours at 77°F (25°C)
• Gray mixed color

Liquid Properties of Rhino 9000

Weight per Gallon, Component "A":7.7 lbs%
Weight per Gallon, Component "B":6.5 lbs
Viscosity:Thixotropic

Directions For Use

Thoroughly mix parts “A” and “B” until a consistent gray color is achieved. If applying to damp, corroded concrete, first apply Rhino 1501 primer (see Rhino 1501 data sheet for more information). Apply mixed material by trowel or putty knife to desired thickness. Allow approximately 8 hours at 77°F to allow “green” strength to develop. Full properties develop in 7 days at typical ambient temperatures.

Cured Properties of Rhino 9000

Peel Strength:34-45 (pli)
Bond Strength, CRS:1,850 (psi)
Bond Strength, Concrete:>400 (psi with 100% concrete failure)
HDT (°F):145
Thermal Conductivity:.44 (BTU/ft/h-ft2 per °F)
Impact Resistance:150 inch/lb
Tensile Strength:5,000-6,000 psi
Tensile Elongation:5%
Tensile Lap Shear:3,000 (psi)
Water Absorption:<1% (24 hours)

How Supplied

Rhino 9000 is packaged in pre-measured kits. FOB San Diego, CA.